Brand Name:YTTORCH

Type:TC1700 Sprinal shape

Application:Small Experimental Electric Furnace

Place of Origin:Yantai,China(Mainland)

Bulk Density:5.8±0.1

Working Temperature:1000℃-1700℃

 

Specification  

YTTORCHTC1700 (Spiral shape) MoSi2 Heating Element

1. High temperature MoSi2 heating element for small experimental electric furnace.

2. Max. working temperature over 1700 ℃

3. Long life combined with ease of replacing failed elements contributes to a high degree of utilization of the furnace and low maintenance costs.

 

Advantage

1. Product has the capabilities to resistance to oxidation and automatically repair, suitable for continued using in any kinds of oxidizing atmospheres.

2.Product is shaped in hot-working process, which keeps the base material in good tenacity and plasticity at high temperature. The geometrical figure, standard and dimension is canonical, may produce any special shape and any dimension to meet the customer requirement.

3.Because of the special technology, welding spot is fast and shock resistance, which dramatically reduced the damaged probability of welding spot by electric current, as well as transit and installation.

4.High density of YT Torch product with faster heating character, element heating rate over 100℃/min

5.Could achieve rapid cooling.

6.Uniform thermal field

7.High purity material heater and come with compact protective layer, good stability in high temperature, avoiding pollution to the furnace.

 

Physical Properties:

Bulk Density-g/cm3

Bending Strength-MPa

Hardness-GPa

Compression Strength-MPa

Water Absorption-%

Heated Elongation-%

5.8±0.1

450

11

>1500

≤0.2%

4

 

Chemical Properties

MoSi2 Heating Element has the ability to withstand oxidation at high temperatures. This is due to the formation of a thin and adhesive protective layer of quartz glass (SiO2) on the surface. When the element temperature over 1700℃, SiO2 protective layer which melting point is 1710℃ was fused, and because of the surface tension, it fused into drops, which is useless. However, when element continue working in oxidizing atmospheres, the SiO2 protective layer is spontaneously rebuilt.

Notice: It is no good to use Molybdenum Disilicide Heating Element for Long-term within a range of 400-700℃, otherwise the element will be powdered by the strong low temperature oxidation.

 

Indicators in Different Atmospheres

 

Atmosphere

TC1700

TC1800

TC1850

TC1900

Air

1700

1800

1830

1850

Nitrogen

1600

1700

1700

1700

Ar Ne Argon, Helium

1600

1700

1700

1700

Dry Hydrogen (dew point)-80℃ 

1150

1150

1150

1150

 Wet Hydrogen (dew point)-20℃

1450

1450

1450

1450

Exogas (e.g. 10% CO2, 50% CO, 15%H2)

1600

1700

1700

1700

Exogas (e.g. 40% CO2, 20% CO)

1400

1450

1450

1450

Cracked and partially burnt ammonia(8%H2

1400

1450

1450

1450

 

Delivery

For any standard and dimensions, delivery within 3 to 15 days without quantitative restriction

Production may be transported by air, boat, railway, Express etc. If production damaged during transportation, we could supply replacement

 

 